'69 Squid Lips

[erebus]

Originally Posted by dirtwheelsfl

If i can wet it out on a table then put into place i will, then hardroll it out.

So when you wet out in place, (not pre-wetted on the table) how do you get good penetration without overworking the glass?
Especially with epoxies?
I find that with thicker resins, if I have to wet out in place I have to roll the heck out of it to get it to wet out evenly, and by the time i'ts wetted out sufficiently I've stretched it or warped it, and end up with hairball ends.
Mostly on vertical or overhead surfaces. Floors I can do.

My go-to utility glass is 1708 biax. Maybe that's too heavy?